Copper Alloy No. C94100
Copper Alloy No. C94100
High Leaded Tin Bronze SAE 94 , CDA 941
ASTM B 505
Chemical Composition % by weight
High Leaded Tin Bronze SAE 94 , CDA 941
ASTM B 505
Chemical Composition % by weight
| Element | Nominal | Minimum | Maximum |
| Aluminum | - | - | .005 |
| Copper | 75.5 | 72 | 79 |
| Iron | - | - | .25 |
| Lead | 20 | 18 | 22 |
| Nickel | - | - | 1 |
| Phosphorus | - | - | .05 |
| Silicon | - | - | .005 |
| Sulfur | - | - | .08 |
| Tin | 5.5 | 4.5 | 6.5 |
| Zinc | - | - | 1 |
Applications
High speed bearings for light loads.
Mechanical Properties
M07 - As Continuous Cast
| Hardness* | Brinell Hardness (500 kg load) | 52 |
| Tensile Strength** | KSI | 25 |
| Yield Strength ** | KSI (0.5% Ext. under load) | 17 |
| Elongation** | % in 2 inch | 16 |
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
| Thermal Conductivity | BTU/ (sq ft-ft-hr-F) | 36.2 |
| Specific Heat | BTU/lb/ºF @ 68F | .09 |
| Thermal Expansion | Per °F from 68 F to 392 F | N/A |
| Density | lb/cu in @ 68 F | .336 |
| Electrical Conductivity* (Annealed) | % IACS @ 68 F | 9 |
| Modulus of Elasticity | KSI | 10,500 |
*Volume basis
Fabrication Practices
| Stress relieving temperature | 500 F or 260 C |
| Time at temperature | 1 hour per inch of section thickness |
| Responds to heat treatment | No |
| Machinability rating (Free Cutting Brass=100) | 75 |
| Suitability for being joined by: | Soldering/Good |
| Brazing/Poor* | |
| Oxyacetylene Welding/Not Recommended | |
| Gas Shielded Arc Welding/Not Recommended | |
| Coated Metal Arc Welding/Not Recommended |