C97600 Nickel Silver Bronze
Copper Alloy No. C97600
Nickel Silver CDA 976 , Dairy Metal , 20% Leaded Nickel Silver ASTM B 505 , ASTM B 271
Chemical Composition % by weight
Nickel Silver CDA 976 , Dairy Metal , 20% Leaded Nickel Silver ASTM B 505 , ASTM B 271
Chemical Composition % by weight
| Element | Nominal | Minimum | Maximum |
| Aluminum | - | - | .005 |
| Antimony | - | - | .25 |
| Copper | 65 | 63 | 67 |
| Iron | - | - | 1.5 |
| Lead | 4 | 3 | 5 |
| Manganese | - | - | 1 |
| Nickel | 20.3 | 19 | 21.5 |
| Phosphorus | - | - | .05 |
| Silicon | - | - | .15 |
| Sulfur | - | - | .08 |
| Tin | 4 | 3.5 | 4.5 |
| Zinc | 6 | 3 | 9 |
Applications for Castings
Marine castings, sanitary fittings, ornamental hardware, valves and pumps.
Mechanical Properties
Typical for 3" dia. continuous cast bar
| Hardness* | Brinell Hardness (500 kg load) | 80 |
| Tensile Strength** | KSI | 45 |
| Yield Strength ** | KSI (0.5% Ext. under load) | 24 |
| Elongation** | % in 2 inch | 20 |
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
| Thermal Conductivity | BTU/ (sq ft-ft-hr-F) | 13 |
| Specific Heat | BTU/lb/ºF @ 68F | .09 |
| Thermal Expansion | Per °F from 68 F to 572 F | .0000093 |
| Density | lb/cu in @ 68 F | .321 |
| Electrical Conductivity* (Annealed) | % IACS @ 68 F | 5 |
| Modulus of Elasticity | KSI | 19,000 |
*Volume basis
Fabrication Practices
| Stress relieving temperature | 500 F or 260 C |
| Time at temperature | 1 hour per inch of section thickness |
| Responds to heat treatment | No |
| Machinability rating (Free Cutting Brass=100) | 70 |
| Suitability for being joined by: | Soldering/Excellent |
| Brazing/Excellent | |
| Oxyacetylene Welding/Not Recommended | |
| Carbon Arc Welding/Not Recommended | |
| Gas Shielded Arc Welding/Not Recommended | |
| Coated Metal Arc Welding/Not Recommended |