C93600 High Leaded Tin Bronze
Copper Alloy No. C93600
High Leaded Tin Bronze CDA 936 , 81-7-12 , Modified SAE 64
Chemical Composition % by weight
High Leaded Tin Bronze CDA 936 , 81-7-12 , Modified SAE 64
Chemical Composition % by weight
Element | Nominal | Minimum | Maximum |
Aluminum | - | - | .005 |
Copper | 81 | 79 | 83 |
Iron | - | - | .20 |
Lead | 12 | 11 | 13 |
Nickel | - | - | 1 |
Phosphorus | - | - | .15 |
Silicon | - | - | .005 |
Sulfur | - | - | .08 |
Tin | 7 | 6 | 8 |
Zinc | - | - | 1 |
Applications
Bearings and bushings
Mechanical Properties
M07 - As Continuous Cast
Hardness* | Brinell Hardness (500 kg load) | 65 |
Tensile Strength** | KSI | 35 |
Yield Strength ** | KSI (0.5% Ext. under load) | 21 |
Elongation** | % in 2 inch | 15 |
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity | BTU/ (sq ft-ft-hr-F) | N/A |
Specific Heat | BTU/lb/ºF @ 68F | .09 |
Thermal Expansion | Per °F from 68 F to 392 F | N/A |
Density | lb/cu in @ 68 F | .325 |
Electrical Conductivity* (Annealed) | % IACS @ 68 F | 11 |
Modulus of Elasticity | KSI | 14,000 |
*Volume basis
Fabrication Practices
Stress relieving temperature | 500 F or 260 C |
Time at temperature | 1 hour per inch of section thickness |
Responds to heat treatment | No |
Machinability rating (Free Cutting Brass=100) | 70 |
Suitability for being joined by: | Soldering/Good |
Brazing/Good* | |
Oxyacetylene Welding/Not Recommended | |
Gas Shielded Arc Welding/Not Recommended | |
Coated Metal Arc Welding/Not Recommended |